耐热钢纤维对高纯度刚玉质浇注料性能的影响

耐火与石灰 ›› 2018, Vol. 43 ›› Issue (1): 14-16.

耐热钢纤维对高纯度刚玉质浇注料性能的影响

杨社彪张晓瑞冯超强

濮阳濮耐高温材料（集团）股份有限公司, 濮阳457100

出版日期:2018-02-10 发布日期:2018-02-10

Effect of heat-resistant steel fiber on the properties of high purity corundum castable refractories

Yang Shebiao Zhang Xiaorui Feng Chaoqiang

Puyang Refractories Group Co.,Ltd., Puyang 457100， China

Online:2018-02-10 Published:2018-02-10

摘要/Abstract

摘要：

研究了外加不同质量分数的耐热钢纤维 (分别为1%、1.5%、2%、2.5%、3%、3.5%)对高纯度刚玉质浇注料性能的影响。综合结果表明：当耐热钢纤维加入量为2.5%时，经过低、中、高温热处理后的高纯度刚玉质浇注料具有较高的体积密度、适宜的线变化、较高的抗折强度和耐压强度；经1 100℃水冷循环5次后试样的残余抗折强度和残余耐压强度较高，其抗热震性能较佳。

Abstract:

In this paper，the effect of heat-resistant steel fiber (1%,1.5%,2%,2.5%,3%,3.5% respectively) on the properties of high purity corundum castable refractories were studied.The results show that when the heat-resistant steel fiber content is 2.5%，after low，medium and high temperature treatment，the high purity corundum castable refractories had higher volume density，suitable linear change,higher flexural strength and compressive strength.After 5 cycles of thermal shock by water cooling at 1 100℃，the residual crushing strength and residual compressive strength is still higher，with satisfactory thermal shock resistance is better.

中图分类号:

TQ175.732

杨社彪张晓瑞冯超强. 耐热钢纤维对高纯度刚玉质浇注料性能的影响[J]. 耐火与石灰, 2018, 43(1): 14-16.

Yang Shebiao Zhang Xiaorui Feng Chaoqiang. Effect of heat-resistant steel fiber on the properties of high purity corundum castable refractories[J]. REFRACTORIES & LIME, 2018, 43(1): 14-16.

[1]	曹喜营. 硅溶胶和磷酸盐类添加剂在无水泥铝镁质耐火浇注料中的应用[J]. 耐火与石灰, 2018, 43(6): 28-33.
[2]	孔祥魁. RH浸渍管浇注料的研究[J]. 耐火与石灰, 2018, 43(5): 3-5.
[3]	徐勇. 高铝质耐火浇注料用烧结助剂[J]. 耐火与石灰, 2018, 43(4): 49-58.
[4]	王晓阳. 抗絮凝剂对高铝低水泥浇注料的影响[J]. 耐火与石灰, 2018, 43(3): 26-28.
[5]	吴占德. 石墨表面涂覆镁铝溶胶-凝胶层的碱性浇注料的耐火性能评估[J]. 耐火与石灰, 2018, 43(1): 40-43.
[6]	孔祥魁. 轧辊离心浇铸用新型端盖浇注料[J]. 耐火与石灰, 2017, 42(6): 14-15.
[7]	吴占德. 含硼酸镁的矿化铝镁水泥结合浇注料[J]. 耐火与石灰, 2017, 42(2): 23-30.
[8]	吴占德. 高性能硅粉凝胶结合无水泥浇注料的进一步开发[J]. 耐火与石灰, 2017, 42(2): 32-35.
[9]	袁本雄邵胜平. 干熄焦炉斜道损坏机理分析及处理[J]. 耐火与石灰, 2017, 42(1): 18-19.
[10]	侯庆冬罗旭东. 纳米莫来石结合耐火浇注料的高温应用研究[J]. 耐火与石灰, 2017, 42(1): 28-34.
[11]	张艳利）贾全利）叶方保）. 矾土基β-SiAlON对Al2O3-MgO浇注料性能的影响[J]. 耐火与石灰, 2016, 41(6): 1-4.
[12]	吴占德. 氧化铝基质和现代分散体系对低水泥浇注料的贡献[J]. 耐火与石灰, 2016, 41(6): 17-21.
[13]	孟庆新. 尖晶石含量对Al2O3-SiC-C质铁沟浇注料性能的影响[J]. 耐火与石灰, 2016, 41(6): 32-38.
[14]	段立中. 对不同水泥种类下含尖晶石高铝浇注料的研究[J]. 耐火与石灰, 2016, 41(6): 39-41.
[15]	吴占德. Al2O3-MgAl2O4和Al2O3-MgO耐火浇注料用抗腐蚀性优化的Al2O3基粘结剂[J]. 耐火与石灰, 2016, 41(6): 48-55.