加热炉水冷梁用耐火浇注料损坏机理及解决措施

耐火与石灰 ›› 2020, Vol. 45 ›› Issue (4): 25-27.

加热炉水冷梁用耐火浇注料损坏机理及解决措施

孙法义王永军刘建中韩尊利

濮阳濮耐高温材料（集团）股份有限公司，濮阳457100

出版日期:2020-08-10 发布日期:2020-08-24

Sun FayiWang YongjunLiu JianzhongHan Zunli

Sun Fayi Wang Yongjun Liu Jianzhong Han Zunli

Puyang Refractories Group Co.,Ltd., Puyang 457100, China

Online:2020-08-10 Published:2020-08-24

摘要/Abstract

摘要： 详细介绍了加热炉水冷梁在设计、施工、烘炉、生产维护过程中，耐火浇注料的损坏原因及损坏机理。为了避免耐火浇注料的损坏，探索出一些合理的技术措施。

关键词: 加热炉, 水冷梁, 耐火浇注料, 损坏机理, 技术措施

Abstract:

This paper introduces the damage reason and mechanism of refractory castable during design,construction,drying-out and productive maintenance of water-cooling beam in heating furnace.To avoid damage to the castable,some reasonable technical measures are explored.

Key words: Heating furnace, Water-cooling beam, Castable, Damage mechanism, , Technology measures

中图分类号:

TQ175.732

孙法义王永军刘建中韩尊利. 加热炉水冷梁用耐火浇注料损坏机理及解决措施[J]. 耐火与石灰, 2020, 45(4): 25-27.

Sun Fayi Wang Yongjun Liu Jianzhong Han Zunli. Sun FayiWang YongjunLiu JianzhongHan Zunli[J]. REFRACTORIES & LIME, 2020, 45(4): 25-27.

[1]	张　显　郝富锁. 新型纳米增强铝质耐火浇注料及预制块在回转窑煅烧带的应用#br#[J]. 耐火与石灰, 2024, 49(1): 17-.
[2]	. 耐火复合材料用氧化铝添加剂的合成与研究[J]. 耐火与石灰, 2023, 48(6): 57-59.
[3]	赵　瑞. 刚玉空心微球对矾土基浇注料物理机械性能和抗热震性的影响[J]. 耐火与石灰, 2023, 48(1): 49-53.
[4]	崔新华. 轧钢加热炉大修烘炉生产实践[J]. 耐火与石灰, 2022, 47(1): 20-22.
[5]	李连洲. 用矿物原料和工业废料生产耐热浇注料[J]. 耐火与石灰, 2021, 46(4): 51-52.
[6]	王永军孙法义刘建中韩尊利. 加热炉用耐火浇注料冬季施工的保温措施[J]. 耐火与石灰, 2020, 45(6): 17-18.
[7]	徐勇. 矾土耐火浇注料性能研究的实验设计[J]. 耐火与石灰, 2018, 43(4): 34-37.
[8]	贺莲花. 含羧酸添加剂的高铝纳米结合耐火浇注料的流变性能研究[J]. 耐火与石灰, 2017, 42(4): 40-44.
[9]	吴占德. 含硼酸镁的矿化铝镁水泥结合浇注料[J]. 耐火与石灰, 2017, 42(2): 23-30.
[10]	孟庆新. 柠檬酸在纳米结合耐火浇注料中的作用和迁移效应[J]. 耐火与石灰, 2015, 40(6): 42-45.
[11]	徐勇. 水泥结合铝镁耐火浇注料的膨胀行为[J]. 耐火与石灰, 2015, 40(341): 34-37.
[12]	李根. 纳米结合耐火浇注料[J]. 耐火与石灰, 2015, 40(2): 45-57.
[13]	李连洲. 浇注料热机械性能的影响[J]. 耐火与石灰, 2014, 39(6): 24-26.
[14]	徐勇. 无水泥耐火浇注料的硬化剂评价[J]. 耐火与石灰, 2014, 39(5): 57-59.
[15]	邵荣丹. 颗粒级配及铝酸钙水泥对全铝质耐火浇注料流变性的影响[J]. 耐火与石灰, 2013, 38(6): 38-44.