具有针状莫来石骨架的高强度多孔陶瓷的制备

耐火与石灰 ›› 2020, Vol. 45 ›› Issue (4): 22-24.

具有针状莫来石骨架的高强度多孔陶瓷的制备

王琳1 杨孟孟2 罗旭东2

1.中冶焦耐（大连）工程技术有限公司, 大连116085； 2.辽宁科技大学材料冶金学院，鞍山114051

出版日期:2020-08-10 发布日期:2020-08-24

High-strength porous ceramic with acicular mullite skeleton

Wang Lin1 Yang Mengmeng2 Luo Xudong2

1.ACRE Coking & Refractory Engineering Consulting Corporation (Dalian),MCC, Dalian 116085, China; 2.School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, China

Online:2020-08-10 Published:2020-08-24

摘要/Abstract

摘要：

在高纯活性莫来石粉体中加入氟化铵（NH4F），制备了具有连续莫来石骨架的自锁结构多孔陶瓷。研究了NH4F对试样显微结构和力学性能的影响，并分别用SEM和抗弯强度进行了表征。NH4F的加入有利于针状莫来石的形成。当添加3% NH4F时，针状莫来石的长径比为14.11，并且形成三维骨架结构，提高了试样的力学性能，强度高达99.43 MPa，气孔率为52.93%。

关键词: 高强度, 多孔陶瓷, 针状莫来石, 三维结构

Abstract:

Self-locking structure porous ceramics with continue mullite framework were prepared by adding NH4F to high purity active mullite powder.The effects of NH4F on micro structure and strength of sample were investigated and characterized by SEM and flexural strength respectively.When 3% NH4F was added, the length-diameter ratio of acicular mullite was 14.11, and the 3D skeleton structure was formed.The mechanical properties of the samples were improved, the strength was up to 99.43 MPa,the porosity was 52.93%.

Key words: High-strength, Porous ceramic, Acicular mullite, 3D skeleton

中图分类号:

TQ175.712.1

王琳杨孟孟罗旭东. 具有针状莫来石骨架的高强度多孔陶瓷的制备[J]. 耐火与石灰, 2020, 45(4): 22-24.

Wang Lin Yang Mengmeng Luo Xudong. High-strength porous ceramic with acicular mullite skeleton[J]. REFRACTORIES & LIME, 2020, 45(4): 22-24.

[1]	张永财. 氧化铝-莫来石-石英多孔可塑耐火材料结构的研究与表征[J]. 耐火与石灰, 2019, 44(2): 40-45.
[2]	侯庆东罗旭东. 利用原位莫来石形成多孔结构的抗致密化浇注料的研究[J]. 耐火与石灰, 2019, 44(1): 46-52.
[3]	朱守丹张永财. 由氧化铝和硼酸制备的硼酸铝陶瓷的显微结构和性能[J]. 耐火与石灰, 2018, 43(6): 55-60.
[4]	刘丽俐. 多孔Al2TiO5-莫来石陶瓷的机械性能和热性能[J]. 耐火与石灰, 2017, 42(4): 58-62.
[5]	吴占德. 多孔Al2O3-莫来石陶瓷的抗热震性[J]. 耐火与石灰, 2017, 42(2): 50-52.
[6]	吴占德. 颗粒稳定泡沫法制备高气孔率氧化铝陶瓷机械性能和损伤容限的研究[J]. 耐火与石灰, 2017, 42(1): 43-49.