RH镁铬砖抗渣侵蚀行为研究

陈希来1  高世远2  冯清蓉1  江群英1   

  1. 1.浙江琰大新材料有限公司, 湖州313100; 2.西宁特殊钢股份有限公司, 西宁810005
  • 出版日期:2021-08-10 发布日期:2021-09-14

Study on corrosion resistance to different slags of RH magnesia-chrome brick

Chen Xilai1  Gao Shiyuan2  Feng Qingrong1  Jiang Qunying1   

  1. 1.Zhejiang Yanda New Material Co.,Ltd., Huzhou 313100, China;2.Xining Special Steel Co.,Ltd., Xining 810005, China
  • Online:2021-08-10 Published:2021-09-14

摘要: 采用热力学软件及静态坩埚抗渣侵蚀试验,研究了RH插入管用镁铬砖抗普钢渣和硅钢渣的侵蚀行为。结果表明: 普钢渣对镁铬砖的侵蚀较小但渗透严重,硅钢渣对镁铬砖侵蚀严重,故建议钢厂在使用同一插入管精炼时可先炼普钢后再炼硅钢,这有利于提高RH插入管的寿命。

关键词: 镁铬砖, RH插入管, 侵蚀行为, 普钢渣, 硅钢渣

Abstract:

Through process simulation with thermodynamic soft ware and static slag corrosion resistance experiment,the corrosion resistance behavior of RH inserted tube magnesia-chrome brick against common steel slag and silicon steel slag in a steel plant were studied.The results show that the corrosion of common steel slag on magnesia-chrome brick is small,but the penetration is serious,and the silicon steel slag has serious corrosion on magnesia-chrome brick.Therefore,it is suggested that steel plants can refine ordinary steel first and then silicon steel when refining with the same RH inserted tube,which is beneficial to prolong the service life of RH inserted tube.

Key words: Magnesia-chrome brick, RH inserted tube, Corrosion behavior, Common steel slag, Silicon steel slag