900 t混铁炉炉衬砌筑优化与使用

耐火与石灰 ›› 2020, Vol. 45 ›› Issue (3): 24-25.

900 t混铁炉炉衬砌筑优化与使用

陈旺学万广强李志勋徐威孟乌鹏

濮阳濮耐高温材料（集团）股份有限公司，濮阳457000

出版日期:2020-06-10 发布日期:2020-06-30

Optimization and application of lining masonry for 900 t metal mixer

Chen Wangxue Wan Guangqiang Li Zhixun Xu Wei Meng Wupeng

Puyang Refractories Group Co.,Ltd., Puyang 457000, China

Online:2020-06-10 Published:2020-06-30

摘要/Abstract

摘要：

介绍了900 t混铁炉炉衬损毁严重部位的情况，分析了损毁原因，通过优化砌筑，提高了混铁炉过铁量和使用寿命以及炼铁效率。

关键词: 混铁炉, 铝碳化硅碳砖, 砌筑, 过铁量

Abstract:

This paper introduces the situation of the seriously damaged parts of the lining of the 900 t metal mixer,analyzes the reasons for the damage,and through optimizing the masonry,improves the iron passing amount and service life of the metal mixer as well as the service efficiency of the ironmaking process.

中图分类号:

TQ175.653

陈旺学万广强李志勋徐威孟乌鹏. 900 t混铁炉炉衬砌筑优化与使用[J]. 耐火与石灰, 2020, 45(3): 24-25.

Chen Wangxue Wan Guangqiang Li Zhixun Xu Wei Meng Wupeng. Optimization and application of lining masonry for 900 t metal mixer[J]. REFRACTORIES & LIME, 2020, 45(3): 24-25.

[1]	李　磊　唐文华　覃芳军　杨俊杰　覃韦崴　张　领. 双膛窑耐火材料砌筑施工优化实践[J]. 耐火与石灰, 2023, 48(6): 51-53.
[2]	王守权王芙云. 硅泥浆在焦炉上的应用[J]. 耐火与石灰, 2021, 46(3): 26-27.
[3]	陈旺学张国星郭朝阳徐威赵永强. 1300t混铁炉内衬材料优化及中修套浇的实践与应用[J]. 耐火与石灰, 2021, 46(2): 15-17.
[4]	王落霞方卓林方义能罗明. MnO对铝碳化硅碳砖侵蚀机理研究[J]. 耐火与石灰, 2020, 45(4): 19-21.
[5]	娄军峰李永力赵永强. 一字型砌筑绘图方法改进研究[J]. 耐火与石灰, 2018, 43(3): 14-15.
[6]	任红霞高俊玲侯金鹏. 转炉各部位耐材使用条件及砌筑方法[J]. 耐火与石灰, 2018, 43(2): 19-21.
[7]	王航民. 浅析焦炭石灰竖炉炉衬损坏机理与选材[J]. 耐火与石灰, 2015, 40(341): 27-28.
[8]	陈勇多志军徐伟王文学. 铁水包透气砖的设计及应用[J]. 耐火与石灰, 2013, 38(2): 7-10.
[9]	张金旭. 砌筑质量对石灰窑的影响[J]. 耐火与石灰, 2011, 36(1): 5-6.
[10]	王少立. 玻璃熔窑蓄热室用镁锆英石耐火材料[J]. 耐火与石灰, 2010, 35(5): 23-26.