电炉渣线砖侵蚀机理及研究进展

耐火与石灰 ›› 2023, Vol. 48 ›› Issue (1): 33-35.

电炉渣线砖侵蚀机理及研究进展

（1．云南濮耐昆钢高温材料有限公司，昆明　650002；

出版日期:2023-02-10 发布日期:2023-03-07

Erosion mechanism and research progress of electric furnace slag line brick

(1. Yunnan Punai Kungang High-temperature Material Co.，Ltd.，Kunming 650002，China；

Online:2023-02-10 Published:2023-03-07

摘要/Abstract

摘要： 电炉渣线磨损是电炉最大的耐火材料问题。本文结合实际生产情况，分析了电炉渣线部位的侵蚀机理，介绍了电炉渣线砖的研究进展及延长电炉渣线寿命的措施。

关键词: 电炉渣线, 镁碳砖, 侵蚀机理

Abstract: Slag line wear of electric furnace is the biggest problem of electric furnace refractories. Based on the actual production situation，the erosion mechanism of the slag line of the electric furnace is analyzed，the research progress of the slag line brick and the measures of slag line life prolongation are summarized

Key words: Electric furnace slag line, Magnesia carbon brick, Erosion mechanism

中图分类号:

TQ175.714

鲁志燕 . 电炉渣线砖侵蚀机理及研究进展[J]. 耐火与石灰, 2023, 48(1): 33-35.

Lu Zhiyan. Erosion mechanism and research progress of electric furnace slag line brick[J]. REFRACTORIES & LIME, 2023, 48(1): 33-35.

[1]	王明慧. 回收料加入量对再生镁碳砖抗渣侵蚀性能的影响[J]. 耐火与石灰, 2021, 46(3): 32-33.
[2]	卢咏明张小红陈海山崔任渠. 低碳镁碳砖热解产物的分析研究[J]. 耐火与石灰, 2021, 46(2): 18-21.
[3]	张艳利王宪贾全利. 炼钢转炉用耐火材料新技术现状及发展趋势[J]. 耐火与石灰, 2021, 46(2): 1-8.
[4]	王落霞方卓林方义能罗明. MnO对铝碳化硅碳砖侵蚀机理研究[J]. 耐火与石灰, 2020, 45(4): 19-21.
[5]	张梁张笑烽. 防氧化剂加入种类对镁碳砖性能的影响[J]. 耐火与石灰, 2020, 45(4): 16-18.
[6]	张艳利王宪贾全利. 炼钢电炉用耐火材料的现状和发展[J]. 耐火与石灰, 2019, 44(3): 7-13.
[7]	王堂玺高洪月王丽娜. 再生镁碳砖的显微结构研究[J]. 耐火与石灰, 2019, 44(2): 23-26.
[8]	魏博. 使用高断裂韧性镁碳砖降低转炉装料炉墙的损伤速度[J]. 耐火与石灰, 2018, 43(5): 32-35.
[9]	闫光辉李军霞. 超低碳镁碳砖在冶炼低碳特钢和不锈钢中的应用[J]. 耐火与石灰, 2018, 43(2): 22-24.
[10]	李英）陶玉婷）曹俊庆）郑连营）曹大力）. 镁碳砖MT-14A在GOR转炉炉底的应用研究[J]. 耐火与石灰, 2018, 43(1): 17-20.
[11]	张艳利谢朝晖. 连铸用MgO-C材料的抗侵蚀性研究[J]. 耐火与石灰, 2017, 42(1): 20-24.
[12]	煤气中HCl对热风炉耐火材料. 煤气中HCl对热风炉耐火材料侵蚀过程的研究[J]. 耐火与石灰, 2015, 40(341): 10-12.
[13]	宋薇) 张国栋) 罗旭东) 刘海啸). 对再生镁碳砖制备过程中碳化铝的研究[J]. 耐火与石灰, 2014, 39(1): 20-23.
[14]	薛燕鹏;）陈玉勇）. A508-3钢液对钢包用含碳耐火材料的侵蚀机理[J]. 耐火与石灰, 2012, 37(6): 15-19.